The Kinetic And Mechanical Aspects Of Hydrogen Induced Failure In Metals PDF Download

This memorandum introduces the problem of delayed, brittle failures associated with hydrogen in steel, particularly high-strength steel. It is intended to help the steel user determine if he has such a problem. The effects of hydrogen on the mechanical properties of steel are dealt with, and the behavior of material susceptible to delayed, brittle failure is described. Also, the effects of such factors as strength level, magnitude of applied stress, hydrogen content, steel composition, test temperature, and strain rate on hydrogen embrittlement and the susceptibility to hydrogen-induced, delayed, brittle failure are discussed. Possible sources of hydrogen in steel and the types of tests useful in determining the susceptibility to delayed failure are outlined. (Author).